Properties :
- Polyethelyne Foam, Produced by Low density Polyethelyne.
- Non toxicity, Fire Rate Class HF-1
- Light weight, Easy installation
- UV Resistance
- Water absorption 0%
- Chemical resistance
|
Usage:
Application and Differences
Filling U-grove during glass window insulation |
Filling welding joints in concrete floors. |
|
|
|
|
Normal Stage |
Expanding Stage |
Shrinking Stage |
|
|
|
Product :
Diameter |
Packing |
mm |
inc |
Length(Metre)/Roll |
Pack(Roll)/Box |
6 |
1/4 |
100 |
35 |
8 |
1/3 |
100 |
20 |
10 |
3/8 |
100 |
16 |
13 |
1/2 |
100 |
12 |
15 |
5/8 |
100 |
8 |
20 |
3/4 |
100 |
5 |
25 |
1 |
50 |
6 |
30 |
1 1/4 |
50 |
4 |
Additional Surface :
|
|
03 |
00 |
Properties :
| Mic-cell Filler Rod and Tube Specification |
| Test Item |
Value |
Unit |
Test Method |
| Density |
41-50 |
kg/m3 |
JIS K6767 |
| Thermal Conductivity |
0.027 |
W/m.K |
ASTM C177 |
| Tensile Strength (Longitudinal Direction) |
44.6 |
N/cm2 |
JIS K6767 |
| ( Lateral Direction) |
38.7 |
N/cm2 |
JIS K6767 |
| Elongation (Longitudinal Direction) |
84.3 |
% |
JIS K6767 |
| ( Lateral Direction) |
77.0 |
% |
JIS K6767 |
| Tear Strength (Longitudinal Direction) |
35.5 |
N/cm |
JIS K6767 |
| ( Lateral Direction) |
29.5 |
N/cm |
JIS K6767 |
| Compression set (at 10% Deformation) |
5.2 |
N/cm2 |
JIS K6767 |
| Working Temperature |
-80 / +85 |
celsius |
- |
| Water Absorption |
0 |
% |
ISO 2896 |
| Moisture Resistance |
 3000 |
|
DIN 52615 |
| Ozone Resistance |
No Crack |
|
ASTM D1149 |
| Ultraviolet |
> 5 years |
|
ASTM G53-88 |
| Flammability |
HF-1 |
|
UL-94 |
| Chemical Resistance |
No Crack |
|
JIS K6767 |
| Toxic |
Non Toxic |
|
|
|
* Under patent no. 21102 |
|
|
|
|
|
Miccell Co.,Ltd. Head Office: Miccell Building Big One Complex 221/1-3 Moo 8, Poochaosamingprai Rd., Samrongklang, Prapradang, Samutprakarn 10130 Thailand.
Tel : +66(02) 380 6960, +66(02) 739 7822 | Fax : +66(02) 380 1084-5 | E-mail : info@miccell.com
www.miccell.com | www.mic-sound.net | www.cooly-cool.com
|